CraftStone™ wall products carry a 25-year limited warranty when used on structures that conform to local building codes and installed according to the manufacturer’s instruction. Warranty is limited to replacement of defective materials only. Damages resulting from building settlement, wall movement, force contact, contact with chemicals or paint, discoloration due to air borne contamination, staining or oxidation, will not be covered under the warranty. Warranty is non-transferable and is only limited to the original purchaser.
Water Repellent
CraftStone™ wall products feature the addition of silicone-based water repellent that greatly enhances the stone’s performance in humid climate.Water Repellent is mixed with the composite material during manufacturing, thus providing a more lasting effect then spray, brush or paint method.
Noncombustible
CraftStone™ products show zero flame spread and zero smoke development.
General Properties
Material Composition : Portland Cement, Light-Weight Aggregates and Iron Oxide Pigments.
Unit Weight : 35 ~ 45kg/m2 (varies according to profile)
Thickness : 20 ~ 40mm (varies according to profile)
Physical Properties
Open Porosity* : < 35%
Compressive Strength* : > 12.0N/mm
Flexural Strength* : > 5.0N/mm2
* Test Reference to NBN EN 1926 (1999), NBN EN 12372 (1999).
Physical Integrity
Frost Resistance+ : 25 cycles of free-thaw, comprising 10 cycles at
–15°C and 15 cycles at –5°C.
– No visual alteration and breakage on all samples.
+ Test Reference to NBN B27-009-1983.
- TAIWAN LABORATORY REPORT
Test Item：
- Compressive Strength：3229 psi Reference to ASTM C39
- Flexural Strength：415 psi Reference to ASTM C78
- Moist Saturation：7.8% Reference to ASTM C140
- Density：91.6 b/ft 3 Reference to ASTM C567
- Shear adhesion strength：144 psi Reference to ASTM C482
- Resistance adhesion strength：203 psi Reference to CNS 12611
- High temperature Resistance: No abnormal Reference to High temperature furnace 800°C in 30min
- Resistance of abrasion using sand blasting method.：0.02g Reference to CNS 3299(Emery scouring 10min)
- Acid resistance(0.5%H2SO4)：No abnormal Reference to CNS 4447
- Alkaline resistance(0.5%HaOH)：No abnormal Reference to CNS 4447
※Test report: Acid resistance and Aklaline resistance been tested having 1 ml of chemical solution on the sample for 24 hours, and then washed with water.
Test Item：
- Compressive Strength：3229 psi
Reference to ASTM C39 - Flexural Strength：415 psi
Reference to ASTM C78 - Moist Saturation：7.8%
Reference to ASTM C140 - Density：91.6 b/ft 3
Reference to ASTM C567 - Shear adhesion strength：144 psi
Reference to ASTM C482 - Resistance adhesion strength：203 psi
Reference to CNS 12611 - High temperature Resistance: No abnormal
Reference to High temperature furnace 800°C in 30min - Resistance of abrasion using sand blasting method.：0.02g
Reference to CNS 3299(Emery scouring 10min) - Acid resistance(0.5%H2SO4)：No abnormal
Reference to CNS 4447 - Alkaline resistance(0.5%HaOH)：No abnormal
Reference to CNS 4447
※Test report: Acid resistance and Aklaline resistance been tested having 1 ml of chemical solution on the sample for 24 hours, and then washed with water.
- BELGIAN BUILDING RESEARCH INSTITUTE
Test Item：
- Compressive Strength：> 12.0 N/mm2
- Flexural Strength：> 5.0 N/mm2
- Moist Saturation：< 13%
- Density：15kg/m3
- Open Porosity：< 35% * Test Reference to NBN EN 1926 (1999), NBN EN 12372 (1999).NBN EN 12372(1999)
- Frost Resistance+ : 25 cycles of free-thaw, comprising 10 cycles at –15°C and 15 cycles at –5°C.
– No visual alteration and breakage on all samples.
※+Test Reference to NBN B27-009-1983.